Stainless steels Manual electrode E385-16 weld fabrication connection
Kopo
E loketse mefuta eohle ea tora e matla ea asiti, tanka, liphaephe le polokelo le lijana tsa lipalangoang, joalo ka 904L.
KIKEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu | |
GB/T MELAO | 0.03 | 1.0-2.5 | 0.90 | 19.5-21.5 | 24.0-26.0 | 4.2-5.2 | 0.03 | 0.02 | 1.2-2.0 | |
MOLAO OA MOLAO | 0.03 | 1.0-2.5 | 0.90 | 19.5-21.5 | 24.0-26.0 | 4.2-5.2 | 0.03 | 0.02 | 1.2-2.0 | |
MOHLALA BOHLOKOA | 0.028 | 1.35 | 0.58 | 20.5 | 25 | 4.85 | 0.02 | 0.001 | 1.70 |
MOSEBETSI OA MECHI:
LETLOTLO | MATLA A KOPA(MPa) | MATLA A KEKETSO(MPa) | IMAPACT BOHLOKO J/℃ | ELONGATION(%) | ||||
GB/T MELAO | - | 520 | - | 28 | ||||
MOLAO OA MOLAO | - | 520 | - | 30 | ||||
MOHLALA BOHLOKOA | - | 600 | - | 37 |
LITLHAKISO TSA TŠEBELETSO TSE KHOTHATSANG:
TLHALOSO EA DIAMETERS(mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
MOTLATSI (Amp) | H/W | 50-75 | 70-95 | 80-120 | 110-160 | 160-190 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |
Titanium calcium stainless steel hand elektrode, sebopeho se seholo ke 20%Cr-25%Ni-5%Mo-2%Cu;
E ka hanela sulfuric acid, phosphoric acid corrosion; E ka hanela ho bola ha acetic acid ka mocheso ofe kapa ofe le ka nako leha e le efe ea khatello tlas'a khatello e tloaelehileng. E ka rarolla ka katleho mathata a pore corrosion, pitting corrosion, crevice corrosion le stress corrosion of halide.
Arc e tsitsitseng, sebopeho se setle, ripple e tiea, ho phatloha ho honyenyane, ho tlosoa ha slag habonolo, ho hanyetsa mollo o motle, ho hanyetsa porosity e ntle.
Ningbo Honest Metal Materials Co, Ltd.ke k'hamphani ea machaba ea litsebi tsa ho cheselletsa ka har'a lipatlisiso le nts'etsopele e ikemetseng, tlhahiso, thekiso le tsamaiso. E thehiloe ka 2020.
Lithane tse 37,000 sekepe se akaretsang sa thepa
Shaanxi Pucheng -50 ℃ propane spherical tank project
Lisebelisoa tsa ho cheselletsa likoloi tsa terene
KIKEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu | |
GB/T MELAO | 0.03 | 1.0-2.5 | 0.90 | 19.5-21.5 | 24.0-26.0 | 4.2-5.2 | 0.03 | 0.02 | 1.2-2.0 | |
MOLAO OA MOLAO | 0.03 | 1.0-2.5 | 0.90 | 19.5-21.5 | 24.0-26.0 | 4.2-5.2 | 0.03 | 0.02 | 1.2-2.0 | |
MOHLALA BOHLOKOA | 0.028 | 1.35 | 0.58 | 20.5 | 25 | 4.85 | 0.02 | 0.001 | 1.70 |
MOSEBETSI OA MECHI:
LETLOTLO | MATLA A KOPA(MPa) | MATLA A KEKETSO(MPa) | IMAPACT BOHLOKO J/℃ | ELONGATION(%) | ||||
GB/T MELAO | - | 520 | - | 28 | ||||
MOLAO OA MOLAO | - | 520 | - | 30 | ||||
MOHLALA BOHLOKOA | - | 600 | - | 37 |
LITLHAKISO TSA TŠEBELETSO TSE KHOTHATSANG:
TLHALOSO EA DIAMETERS(mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
MOTLATSI (Amp) | H/W | 50-75 | 70-95 | 80-120 | 110-160 | 160-190 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |