Kopo
E loketse bakeng sa tjheseletsa 18% Cr-8% Ni-Nb tšepe e sa hloekang (SUS347) le 18% Cr-8% Ni-Ti tšepe e sa hloekang (sus321) indastering ea petrochemical, sekepe sa khatello, mechine ea lijo, mechine ea bongaka, manyolo a lik'hemik'hale le liindasteri tse ling.
KIKEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | tse ling | |
GB/T MELAO | 0.04 | 0.5-2,5 | 1.00 | 18.0-21.0 | 9.0-11.0 | 0.75 | 0.04 | 0.03 | Cu0.75/Nb:8C-1.00 | |
MOLAO OA MOLAO | 0.08 | 0.5-2,5 | 1.00 | 18.0-21.0 | 9.0-11.0 | 0.75 | 0.04 | 0.03 | Cu0.75/Nb:8C-1.00 | |
MOHLALA BOHLOKOA | 0.033 | 0.84 | 0.69 | 18.7 | 9.5 | 0.1 | 0.027 | 0.005 | Cu0.22/Nb0.50 |
MOSEBETSI OA MECHI:
LETLOTLO | MATLA A KOPA(MPa) | MATLA A KEKETSO(MPa) | IMAPACT BOHLOKO J/℃ | ELONGATION(%) | ||||
GB/T MELAO | - | 510 | - | 25 | ||||
MOLAO OA MOLAO | - | 520 | - | 30 | ||||
MOHLALA BOHLOKOA | - | 615 | - | 36 |
LITLHAKISO TSA TŠEBELETSO TSE KHOTHATSANG:
TLHALOSO EA DIAMETERS(mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
MOTLATSI (Amp) | H/W | 50-75 | 70-95 | 80-120 | 110-160 | 160-190 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |
Titanium calcium stainless steel hand electrode, motsoako o ka sehloohong ke carbon e tlaase 18% Cr-9% Ni-Nb; Ha Nb e eketsoa motheong oa 308, carbon content e tlaase ka nako e le 'ngoe, e ka ntlafatsang ka katleho ho hanyetsa kutu. , haholo-holo ts'ebetso ea intergranular corrosion.
Arc e tsitsitseng, sebopeho se setle, ripple e tiea, ho phatloha ho honyenyane, ho tlosoa ha slag habonolo, ho hanyetsa mollo o motle, ho hanyetsa porosity e ntle.
Ningbo Honest Metal Materials Co, Ltd.ke k'hamphani ea machaba ea litsebi tsa ho cheselletsa ka har'a lipatlisiso le nts'etsopele e ikemetseng, tlhahiso, thekiso le tsamaiso. E thehiloe ka 2020.
Xinjiang Kela 2 projeke ea setsi sa tšebetso se bohareng
Lisebelisoa tsa ho cheselletsa lijana
Morero oa tanka ea Gansu Lanke Petrochemical -50 ℃ propane spherical tank
KIKEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | tse ling | |
GB/T MELAO | 0.04 | 0.5-2,5 | 1.00 | 18.0-21.0 | 9.0-11.0 | 0.75 | 0.04 | 0.03 | Cu0.75/Nb:8C-1.00 | |
MOLAO OA MOLAO | 0.08 | 0.5-2,5 | 1.00 | 18.0-21.0 | 9.0-11.0 | 0.75 | 0.04 | 0.03 | Cu0.75/Nb:8C-1.00 | |
MOHLALA BOHLOKOA | 0.033 | 0.84 | 0.69 | 18.7 | 9.5 | 0.1 | 0.027 | 0.005 | Cu0.22/Nb0.50 |
MOSEBETSI OA MECHI:
LETLOTLO | MATLA A KOPA(MPa) | MATLA A KEKETSO(MPa) | IMAPACT BOHLOKO J/℃ | ELONGATION(%) | ||||
GB/T MELAO | - | 510 | - | 25 | ||||
MOLAO OA MOLAO | - | 520 | - | 30 | ||||
MOHLALA BOHLOKOA | - | 615 | - | 36 |
LITLHAKISO TSA TŠEBELETSO TSE KHOTHATSANG:
TLHALOSO EA DIAMETERS(mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
MOTLATSI (Amp) | H/W | 50-75 | 70-95 | 80-120 | 110-160 | 160-190 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |