Stainless Steels Manual Electrode E316L-17 tjheseletsa e kholo e nang le mokelikeli oa khase
THEKNOLOJI CHESE
Se lumelle lipotso
Tsoela pele ho u hlorisa
Arc ho hloka botsitso
Ho bopa ho sa kgahliseng
Spatter e feteletseng
E sebelisoa haholo ho manyolo, urea, petrochemical
thepa ea tlhahiso kapa polokelo sebopeho sa bohlokoa
Pitsa mofuta oa tšepe e se nang tšepe elektrode ea letsoho, jet arc, e ka sehloohong
karolo e tlase C-18%Cr-12%Ni-2%Mo, e babatsehang ntlha corrosion resistanc.
Ripple hantle
Ts'ebetso e ntle ea welding, khanyetso ea crack, khanyetso ea porosity e ntle haholo
Ho roala ho na le khanyetso e ntle ea mollo, thepa e tsitsitseng ea tšepe e kopantsoeng le sekhahla se phahameng sa X-Rav.
Slagging e bonolo
Parameter ea sehlahisoa
KIKEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | Tse ding |
GB/T MELAO | 0.029 | 0.61 | 0.78 | 0.029 | 0.006 | 11.58 | 18.4 | 2.5 | 0.07 | - |
MOSEBETSI OA MECHI:
LETLOTLO | MATLA A KOPA(MPa) | MATLA A KEKETSO(MPa) | IMAPACT BOHLOKO J/℃ | Phekolo ea mocheso °C*h | ||||
GB/T MELAO | 580 | 38 | - | - |
LITLHAKISO TSA TŠEBELETSO TSE KHOTHATSANG:
TLHALOSO EA DIAMETERS(mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
MOTLATSI (Amp) | H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |
Tšehetso ea fektheri
Sehlahisoa se loketse bakeng sa a
mefuta e mengata ea likopo
THEKNOLOJI CHESE
85000 m3 E kholo Haholo
Ethane Vinyl Carrier (VLEC)
-
Guangxi Huayi
methanol dehydrating tower
-
Shaanxi Pucheng -50 ℃
propane spherical tank project
KIKEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | Tse ding |
GB/T MELAO | 0.029 | 0.61 | 0.78 | 0.029 | 0.006 | 11.58 | 18.4 | 2.5 | 0.07 | - |
MOSEBETSI OA MECHI:
LETLOTLO | MATLA A KOPA(MPa) | MATLA A KEKETSO(MPa) | IMAPACT BOHLOKO J/℃ | Phekolo ea mocheso °C*h | ||||
GB/T MELAO | 580 | 38 | - | - |
LITLHAKISO TSA TŠEBELETSO TSE KHOTHATSANG:
TLHALOSO EA DIAMETERS(mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
MOTLATSI (Amp) | H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |