Nickel alloys Manual electrode ENi-1 weld fabrication making
KIKEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Ni | Fe | Ti | Cu | P | S |
GB/T MELAO | 0.10 | 0.75 | 1.20 | ≥92 | 0.70 | 1.0-4.0 | 0.20 | 0.02 | 0.015 |
MOLAO OA MOLAO | 0.10 | 0.75 | 1.25 | ≥92 | 0.75 | 1.0-4.0 | 0.25 | 0.03 | 0.02 |
MOHLALA BOHLOKOA | 0.046 | 0.06 | 0.82 | 95.5 | 0.12 | 2.7 | 0.01 | 0.007 | 0.001 |
MOSEBETSI OA MECHI:
LETLOTLO | MATLA A KOPA(MPa) | MATLA A KEKETSO(MPa) | IMAPACT BOHLOKO J/℃ | ELONGATION(%) | ||||
GB/T MELAO | 200 | 410 | - | 18 | ||||
MOLAO OA MOLAO | - | 410 | - | 20 | ||||
MOHLALA BOHLOKOA | 310 | 435 | - | 29 |
LITLHAKISO TSA TŠEBELETSO TSE KHOTHATSANG:
TLHALOSO EA DIAMETERS(mm) | 2.6*300 | 3.2*350 | 4.0*350 | |||||||
MOTLATSI (Amp) | H/W | 65-95 | 70-115 | 95-145 |
Elektrode ea letsoho ea Titanium-calcium, sebopeho sa lebitso (lekholong ka boima ba 'mele) ke 95Ni-2.5Ti.
Arc e tsitsitseng, sebopeho se setle, ho phatloha ho honyenyane, ho tlosoa ha slag habonolo, ho hanyetsa porosity e ntle.
Tšepe e kopantsoeng e na le thepa e ntle ea mochini, ho hanyetsa mocheso, ho hanyetsa ho bola, ho kopana le ho hanyetsa ho phatloha.
Lisebelisoa tsa welding tsa Cr-Mo le lisebelisoa tsa welding tsa electrode li sebelisoa haholo lisebelisoa tsa ho hloekisa peterole.
-
Lithane tse 158,000 tsa sekepe sa Suez
Supercore SG
KIKEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Ni | Fe | Ti | Cu | P | S |
GB/T MELAO | 0.10 | 0.75 | 1.20 | ≥92 | 0.70 | 1.0-4.0 | 0.20 | 0.02 | 0.015 |
MOLAO OA MOLAO | 0.10 | 0.75 | 1.25 | ≥92 | 0.75 | 1.0-4.0 | 0.25 | 0.03 | 0.02 |
MOHLALA BOHLOKOA | 0.046 | 0.06 | 0.82 | 95.5 | 0.12 | 2.7 | 0.01 | 0.007 | 0.001 |
MOSEBETSI OA MECHI:
LETLOTLO | MATLA A KOPA(MPa) | MATLA A KEKETSO(MPa) | IMAPACT BOHLOKO J/℃ | ELONGATION(%) | ||||
GB/T MELAO | 200 | 410 | - | 18 | ||||
MOLAO OA MOLAO | - | 410 | - | 20 | ||||
MOHLALA BOHLOKOA | 310 | 435 | - | 29 |
LITLHAKISO TSA TŠEBELETSO TSE KHOTHATSANG:
TLHALOSO EA DIAMETERS(mm) | 2.6*300 | 3.2*350 | 4.0*350 | |||||||
MOTLATSI (Amp) | H/W | 65-95 | 70-115 | 95-145 |
Ngola molaetsa wa hao mona mme o re romele wona