Li-alloys tsa Nickel TIG ERNi-1 Khokahano ea ho rekisa
KIKEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Ti | P | S |
GB/T MELAO | 0.15 | 1.00 | 0.70 | - | ≥92 | - | 1.0 | 2.0-3.5 | 0.03 | 0.015 |
MOLAO OA MOLAO | 0.15 | 1.00 | 0.75 | - | ≥93 | - | 1.0 | 2.0-3.5 | 0.03 | 0.015 |
MOHLALA BOHLOKOA | 0.005 | 0.48 | 0.26 | 0.46 | 94.69 | 0.001 | 0.07 | 2.95 | 0.001 | 0.001 |
MOSEBETSI OA MECHI:
LETLOTLO | MATLA A KOPA(MPa) | MATLA A KEKETSO(MPa) | IMAPACT BOHLOKO J/℃ | ELONGATION(%) | ||||
GB/T MELAO | - | - | - | - | ||||
MOLAO OA MOLAO | - | - | - | - | ||||
MOHLALA BOHLOKOA | - | 550 | 276/-196 | 36 |
Mohala o hloekileng oa khase ea nickel, sebopeho sa lebitso ke 96%Ni-3%Ti.
Ka lebaka la ho eketsoa ha ntho e lekaneng ea Ti, porosity e ka fokotsoa ka katleho ts'ebetsong ea welding.
Arc e tsitsitseng, sebopeho se setle, phallo e ntle ea tšepe e qhibilihisitsoeng, e nang le ts'ebetso e ntle ea ts'ebetso ea welding.
-
Lithane tse 37,000 sekepe se akaretsang sa thepa
-
JU2000E jack-up cheka rig
-
Lebokose la ente ea polokeho
KIKEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Ti | P | S |
GB/T MELAO | 0.15 | 1.00 | 0.70 | - | ≥92 | - | 1.0 | 2.0-3.5 | 0.03 | 0.015 |
MOLAO OA MOLAO | 0.15 | 1.00 | 0.75 | - | ≥93 | - | 1.0 | 2.0-3.5 | 0.03 | 0.015 |
MOHLALA BOHLOKOA | 0.005 | 0.48 | 0.26 | 0.46 | 94.69 | 0.001 | 0.07 | 2.95 | 0.001 | 0.001 |
MOSEBETSI OA MECHI:
LETLOTLO | MATLA A KOPA(MPa) | MATLA A KEKETSO(MPa) | IMAPACT BOHLOKO J/℃ | ELONGATION(%) | ||||
GB/T MELAO | - | - | - | - | ||||
MOLAO OA MOLAO | - | - | - | - | ||||
MOHLALA BOHLOKOA | - | 550 | 276/-196 | 36 |