KIKEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S |
GB/T MELAO | - | - | - | - | - | - | - | - |
MOLAO OA MOLAO | - | - | - | - | - | - | - | - |
MOHLALA BOHLOKOA | 0.06 | 1.70 | 0.3 | 0.02 | 0.8 | 0.8 | 0.01 | 0.005 |
MOSEBETSI OA MECHI:
LETLOTLO | MATLA A KOPA(MPa) | MATLA A KEKETSO(MPa) | IMAPACT BOHLOKO J/℃ | ELONGATION(%) | Kalafo ea mocheso°Cxh | |||||
GB/T MELAO | - | - | - | - | AW | |||||
MOLAO OA MOLAO | 410 | 550-700 | 27/-20 | 20 | AW | |||||
MOHLALA BOHLOKOA | 540 | 660 | 120/-20 | 25 | AW |
LITLHAKISO TSA TŠEBELETSO TSE KHOTHATSANG:
TLHALOSO EA DIAMETERS(mm) | 1.6 | ||||
Volt | 38-42 | ||||
Amp | 360-400 | ||||
Bolelele bo omileng (mm) | 20-30 | ||||
Phallo ea khase(l/min) | 25-35 |
E na le lebelo le phahameng la ho qhibiliha, 'me arc e tsitsitse haholo.
Ho sebelisa mokhoa o bonolo oa welding, ho ka ba bonolo haholo ho phethela welding.
Bokgoni bo phahameng.
-
10000TEU sekepe sa lijana
-
Shandong Nuclear Power CV20
-
Guangxi Huayi esterification Tower
KIKEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S |
GB/T MELAO | - | - | - | - | - | - | - | - |
MOLAO OA MOLAO | - | - | - | - | - | - | - | - |
MOHLALA BOHLOKOA | 0.06 | 1.70 | 0.3 | 0.02 | 0.8 | 0.8 | 0.01 | 0.005 |
MOSEBETSI OA MECHI:
LETLOTLO | MATLA A KOPA(MPa) | MATLA A KEKETSO(MPa) | IMAPACT BOHLOKO J/℃ | ELONGATION(%) | Kalafo ea mocheso°Cxh | |||||
GB/T MELAO | - | - | - | - | AW | |||||
MOLAO OA MOLAO | 410 | 550-700 | 27/-20 | 20 | AW | |||||
MOHLALA BOHLOKOA | 540 | 660 | 120/-20 | 25 | AW |
LITLHAKISO TSA TŠEBELETSO TSE KHOTHATSANG:
TLHALOSO EA DIAMETERS(mm) | 1.6 | ||||
Volt | 38-42 | ||||
Amp | 360-400 | ||||
Bolelele bo omileng (mm) | 20-30 | ||||
Phallo ea khase(l/min) | 25-35 |