KIKEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
GB/T MELAO | 0.12 | 0.5-1.30 | 0.20-0.80 | 0.45-0,75 | 0.30-0,80 | - | 0.03 | 0.03 | 0.30-0,75 |
MOLAO OA MOLAO | 0.12 | 0.5-1.30 | 0.35-0,80 | 0.45-0,70 | 0.40-0,80 | - | 0.03 | 0.03 | 0.30-0,75 |
MOHLALA BOHLOKOA | 0.03 | 1.00 | 0.4 | 0.5 | 0.7 | 0.01 | 0.01 | 0.005 | 0.39 |
MOSEBETSI OA MECHI:
LETLOTLO | MATLA A KOPA(MPa) | MATLA A KEKETSO(MPa) | IMAPACT BOHLOKO J/℃ | ELONGATION(%) | Kalafo ea mocheso°Cxh | |||||
GB/T MELAO | 460 | 550-74 | 27/-40 | 17 | AW | |||||
MOLAO OA MOLAO | 470 | 550-690 | 27/-30 | 19 | AW | |||||
MOHLALA BOHLOKOA | 575 | 635 | 112/-40 | 26 | AW |
LITLHAKISO TSA TŠEBELETSO TSE KHOTHATSANG:
TLHALOSO EA DIAMETERS(mm) | 1.2 | 1.4 | 1.6 | |||||||
Volt | 25-32 | 24-36 | 25-40 | |||||||
Amp | 150-300 | 170-360 | 200-400 | |||||||
Bolelele bo omileng (mm) | 15-20 | 15-20 | 18-25 | |||||||
Phallo ea khase(l/min) | 15-25 | 15-25 | 15-25 |
![02](http://www.welding-honest.com/uploads/0256.jpg)
The arc e bonolo ebile e tsitsitse, ho fokotseha ho fokolang, ho theha hantle, ho tlosoa ha slag hantle.
Soot e nyane, ke ts'ebetso ea ts'ebetso ea welding ea Yueermin feela.
![03](http://www.welding-honest.com/uploads/0345.jpg)
![01](http://www.welding-honest.com/uploads/0170.jpg)
Tšepe e kopantsoeng e na le Cu, Ni, Cr, kahoo khanyetso ea kutu ea sepakapaka e ntle, e hanyetsana hantle haholo le ho phatloha.
![未标题-8](http://www.welding-honest.com/uploads/未标题-82.jpg)
![未标题-7](http://www.welding-honest.com/uploads/未标题-72.jpg)
![03](http://www.welding-honest.com/uploads/0340.jpg)
![04](http://www.welding-honest.com/uploads/0424.jpg)
![b0780de687c3deca16d616279ad5fd6](http://www.welding-honest.com/uploads/b0780de687c3deca16d616279ad5fd6.png)
![04](http://www.welding-honest.com/uploads/0426.jpg)
![07](http://www.welding-honest.com/uploads/0712.jpg)
![06](http://www.welding-honest.com/uploads/0615.jpg)
![05](http://www.welding-honest.com/uploads/0519.jpg)
![01](http://www.welding-honest.com/uploads/0174.jpg)
![02](http://www.welding-honest.com/uploads/0260.jpg)
![03](http://www.welding-honest.com/uploads/0349.jpg)
-
Morero oa LNG oa Canada
Supercore SG
-
Hainan Huasheng phenol recovery tower
![577445SDA01](http://www.welding-honest.com/uploads/577445SDA01.jpg)
KIKEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
GB/T MELAO | 0.12 | 0.5-1.30 | 0.20-0.80 | 0.45-0,75 | 0.30-0,80 | - | 0.03 | 0.03 | 0.30-0,75 |
MOLAO OA MOLAO | 0.12 | 0.5-1.30 | 0.35-0,80 | 0.45-0,70 | 0.40-0,80 | - | 0.03 | 0.03 | 0.30-0,75 |
MOHLALA BOHLOKOA | 0.03 | 1.00 | 0.4 | 0.5 | 0.7 | 0.01 | 0.01 | 0.005 | 0.39 |
MOSEBETSI OA MECHI:
LETLOTLO | MATLA A KOPA(MPa) | MATLA A KEKETSO(MPa) | IMAPACT BOHLOKO J/℃ | ELONGATION(%) | Kalafo ea mocheso°Cxh | |||||
GB/T MELAO | 460 | 550-74 | 27/-40 | 17 | AW | |||||
MOLAO OA MOLAO | 470 | 550-690 | 27/-30 | 19 | AW | |||||
MOHLALA BOHLOKOA | 575 | 635 | 112/-40 | 26 | AW |
LITLHAKISO TSA TŠEBELETSO TSE KHOTHATSANG:
TLHALOSO EA DIAMETERS(mm) | 1.2 | 1.4 | 1.6 | |||||||
Volt | 25-32 | 24-36 | 25-40 | |||||||
Amp | 150-300 | 170-360 | 200-400 | |||||||
Bolelele bo omileng (mm) | 15-20 | 15-20 | 18-25 | |||||||
Phallo ea khase(l/min) | 15-25 | 15-25 | 15-25 |